NJMKT Carbon Fiber Impregnation Adhesive (MKT-CFR/A)

NJMKT Carbon Fiber Impregnation Adhesive (MKT-CFR/A)

Main Components: Modified epoxy resin, other additives

Component A: Component B = 2:1

Share Facebook Twitter LinkedIn Pinterest Google+ Addthis

    Features:

    ● Component A: Component B = 2:1, two-component carbon fiber adhesive, modified epoxy adhesive

    ● Nearly odorless, non-toxic, there is almost no shrinkage during curing process

    ● Good resistance to weather, high temperature, age, corrosion, etc., excellent mechanical performance and high durability 

    ● strong permeability, high tensile strength and bonding strength. 

    ● Fast and easy stirring ensures accurate mixing proportion 2:1, when properly mixed, adhesive will be an even color for use

    ● NJMKT carbon fiber adhesive specialized for low temperature can still keep a perfect permeability in the temperature of -5℃, you can choose our special low temperature adhesive depending on your installation ● Mixed adhesive should be used up within 20~60 minutes (depending on specific ambient temperature)

    ● The density is about 1.15~1.20 g/cm3 (cured ), gel time is about 3~8 hours

    ● Moderate viscosity, meet the requirement of bonding thickness (1.5±0.5) mm for carbon fiber composite materials in "Code for Acceptance of Construction Quality of Strengthening Building Structures"


    ● Adhesion of various fibers, such as carbon fiber, basalt fiber, glass fiber, aramid fiber (kevlar fiber), etc.

    ● Widely used for carbon fiber materials, high initial adhesion and sustained tensile strength, especially strong permeability for carbon fiber sheet

    ● Wide working temperature range: 5℃~ 40℃, available in all working conditions, including dry, wet and underwater environment

    ● Excellent thixotropy and nearly non-drip for horizontal, vertical and overhead applications, low flowability for vertical construction



    Operating environment:

    *Dry condition

    *Wet condition

    *Underwater condition


    Caution:

    ● Mix the adhesive well according to its weight proportion strictly

    ● Construction crew should take steps of protective measures to keep it from eyes

    ● Remaining adhesive cannot be poured into original barrels


    Packing: 

    ● Two kinds of package, 30kg (A+B two barrels)/pair; 15kg (A+B two barrels)/pair


    Storage:

    ● Shelf life: At least 12 months from date of manufacture in unopened container when store in dry and well-ventilated place. Please store in ambient temperature from 5 ℃ to 40 ℃, away from open flame, heating devices

    ● Adhesive specialized for low temperature can be stored in ambient temperature from -5 ℃ to 40 ℃

    ● Handle with care, protect from rain, sunlight and place upward during loading and unloading transportation


    Standard: GB50367-2013, GB50728-2011

    NJMKT promises to meet the technical requirements of the following GB50367-2013 "Design code for concrete structure reinforcement" and GB50728-2011 "Technical code for safety identification of reinforcement materials for engineering structures". 


    NJMKT Carbon Fiber Impregnation Adhesive (MKT - CFR / A)
    NO.Item NameTechnical Specification (Adhesive Grade A)Test ResultSingle item assessment
    1Tensile strength (MPa)C3842Qualified
    2Tensile modulus of elasticity (MPa)≥ 24002635Qualified
    3Elongation (%)≥ 1.55.03Qualified
    4Bending strength (MPa)≥ 50, and without brittle failure51, and without brittle failureQualified
    5Compressive strength (MPa)≥ 7070.3Qualified
    6Steel - steel nominal value of tensile and shear strength (MPa)≥ 1418.1Qualified
    7Steel - steel T impact stripping length (mm)≤ 206.7Qualified
    8Steel - concrete C45 positive bonding tensile strength (MPa)≥ 2.5, and concrete cohesive failure3.4, and concrete cohesive failureQualified
    9Heat distortion temperature (℃)≥ 6565.3Qualified
    10Content of non - volatile (%)≥ 9999.4Qualified
    11Damp - heat aging resistance performance (7D) (%)Adhesive Grade A: Steel - steel bonding shear strength decreased ≤ 8strength decreased 7.4Qualified
    Note

    1. Steel-steel T impact stripping length (mm): impact height is 305mm, impact object quality is 903g, sample surface is sand blasting treatment.

    2. Damp-heat aging resistance performance (7D): after 7 days the sample is cured, then boil in 80℃ water container for 7days.

Description

Features:

● Component A: Component B = 2:1, two-component carbon fiber adhesive, modified epoxy adhesive

● Nearly odorless, non-toxic, there is almost no shrinkage during curing process

● Good resistance to weather, high temperature, age, corrosion, etc., excellent mechanical performance and high durability 

● strong permeability, high tensile strength and bonding strength. 

● Fast and easy stirring ensures accurate mixing proportion 2:1, when properly mixed, adhesive will be an even color for use

● NJMKT carbon fiber adhesive specialized for low temperature can still keep a perfect permeability in the temperature of -5℃, you can choose our special low temperature adhesive depending on your installation ● Mixed adhesive should be used up within 20~60 minutes (depending on specific ambient temperature)

● The density is about 1.15~1.20 g/cm3 (cured ), gel time is about 3~8 hours

● Moderate viscosity, meet the requirement of bonding thickness (1.5±0.5) mm for carbon fiber composite materials in "Code for Acceptance of Construction Quality of Strengthening Building Structures"


Applications

● Adhesion of various fibers, such as carbon fiber, basalt fiber, glass fiber, aramid fiber (kevlar fiber), etc.

● Widely used for carbon fiber materials, high initial adhesion and sustained tensile strength, especially strong permeability for carbon fiber sheet

● Wide working temperature range: 5℃~ 40℃, available in all working conditions, including dry, wet and underwater environment

● Excellent thixotropy and nearly non-drip for horizontal, vertical and overhead applications, low flowability for vertical construction



Functionality

Operating environment:

*Dry condition

*Wet condition

*Underwater condition


Caution:

● Mix the adhesive well according to its weight proportion strictly

● Construction crew should take steps of protective measures to keep it from eyes

● Remaining adhesive cannot be poured into original barrels


Packing: 

● Two kinds of package, 30kg (A+B two barrels)/pair; 15kg (A+B two barrels)/pair


Storage:

● Shelf life: At least 12 months from date of manufacture in unopened container when store in dry and well-ventilated place. Please store in ambient temperature from 5 ℃ to 40 ℃, away from open flame, heating devices

● Adhesive specialized for low temperature can be stored in ambient temperature from -5 ℃ to 40 ℃

● Handle with care, protect from rain, sunlight and place upward during loading and unloading transportation

Project


Technical Data

Standard: GB50367-2013, GB50728-2011

NJMKT promises to meet the technical requirements of the following GB50367-2013 "Design code for concrete structure reinforcement" and GB50728-2011 "Technical code for safety identification of reinforcement materials for engineering structures". 


NJMKT Carbon Fiber Impregnation Adhesive (MKT - CFR / A)
NO.Item NameTechnical Specification (Adhesive Grade A)Test ResultSingle item assessment
1Tensile strength (MPa)C3842Qualified
2Tensile modulus of elasticity (MPa)≥ 24002635Qualified
3Elongation (%)≥ 1.55.03Qualified
4Bending strength (MPa)≥ 50, and without brittle failure51, and without brittle failureQualified
5Compressive strength (MPa)≥ 7070.3Qualified
6Steel - steel nominal value of tensile and shear strength (MPa)≥ 1418.1Qualified
7Steel - steel T impact stripping length (mm)≤ 206.7Qualified
8Steel - concrete C45 positive bonding tensile strength (MPa)≥ 2.5, and concrete cohesive failure3.4, and concrete cohesive failureQualified
9Heat distortion temperature (℃)≥ 6565.3Qualified
10Content of non - volatile (%)≥ 9999.4Qualified
11Damp - heat aging resistance performance (7D) (%)Adhesive Grade A: Steel - steel bonding shear strength decreased ≤ 8strength decreased 7.4Qualified
Note

1. Steel-steel T impact stripping length (mm): impact height is 305mm, impact object quality is 903g, sample surface is sand blasting treatment.

2. Damp-heat aging resistance performance (7D): after 7 days the sample is cured, then boil in 80℃ water container for 7days.