Features:
● High tensile strength and light weight
● Abrasion and corrosion resistance
● High electric conductivity
● High elastic modulus
● High temperature resistant
● Type : 1K, 3K,6K,12K
● Weave pattern: bidirectional twill and plain
Carbon fiber sheet is the most commonly used composite fabric with applications in present international industrial area. It has features of light weight, high strength, high modulus, high-temperature resistance, corrosion and fatigue resistance...better than those of steel, aluminum. The products made of carbon fiber have outstanding physical and chemical properties, making them widely applied in various fields.
● Aerospace area: fuselage, rudder, rocket engine housing, missile diffuser, solar panel, etc.
● Sports: Automobile parts, motorcycle parts, fishing rod, baseball bat, ski board, yacht, badminton racket
● Industry: engine parts, concrete structure reinforcement materials, fan blade, transmission shaft, electrical components etc.
● Firefighting: suitable for special types of high-grade fireproof suits for army forces, fire protection forces, steel mill,etc.
● Construction reinforcement, increase building load-bearing, material aging, structural cracks processing
● Concrete strength grade is lower than the design value
● Harsh environment service components repair and protection
● Other industrial products and many other fields
Storage:
● Carbon fiber sheet should be stored in dry and well-ventilated place and protect from sunlight.
1K means 1 carbon yarn contains 1000 filaments, 2K means 2000 filaments, and so on. We have 1K/3K/6K/12K carbon fiber fabric. The smaller K is, more complicated the production process is! so the small K carbon fiber fabric is more expensive.
There are unidirectional carbon fiber fabric used as reinforcement clothing for bridge, road and building. The two-way cabon fiber fabric are woven with Plain and Twill style, we have 120gsm/140gsm/200gsm/240gsm/280gsm/320gsm/400gsm/480gsm/640gsm for choosing.
Mankat will provide the best products and solutions, until the customer was satisfied
| Type | Tensile strength | Tensile modulus | Density | Warp and weft | Thickness | Width | Length |
| Mpa | Gpa | g/cm3 | filament/cm2 | mm | cm | m | |
| ＞3300 | ＞220 | 160 | 4×4 | 0.3 | 100 | 100 | |
| ＞3300 | ＞220 | 200 | 5×5 | 0.26 | 100 | 100 | |
| 3k plain | ＞3300 | ＞220 | 220 | 5.5×5.5 | 0.32 | 100 | 100 |
| ＞3300 | ＞220 | 240 | 6×6 | 0.34 | 100 | 100 | |
| ＞3300 | ＞220 | 260 | 6×7 | 0.34 | 100 | 100 | |
| ＞3300 | ＞220 | 160 | 4×4 | 0.26 | 100 | 100 | |
| ＞3300 | ＞220 | 200 | 5×5 | 0.3 | 100 | 100 | |
| 3k twill | ＞3300 | ＞220 | 220 | 5.5×5.5 | 0.29 | 100 | 100 |
| ＞3300 | ＞220 | 240 | 6×6 | 0.32 | 100 | 100 | |
| ＞3300 | ＞220 | 260 | 6×7 | 0.33 | 100 | 100 | |
| ＞3300 | ＞220 | 280 | 7×7 | 0.34 | 100 | 100 | |
| 6k plain | ＞3300 | ＞220 | 300 | 4×4 | 0.36 | 100 | 100 |
| ＞3300 | ＞220 | 400 | 5×5 | 0.42 | 100 | 100 | |
| 6k twill | ＞3300 | ＞220 | 300 | 4×4 | 0.36 | 100 | 100 |
| ＞3300 | ＞220 | 400 | 5×5 | 0.42 | 100 | 100 | |
| ＞3300 | ＞220 | 400 | 2.5×2.5 | 0.46 | 100 | 100 | |
| 12k plain | ＞3300 | ＞220 | 480 | 3×3 | 0.52 | 100 | 100 |
| ＞3300 | ＞220 | 560 | 3.5×3.5 | 0.56 | 100 | 100 | |
| ＞3300 | ＞220 | 580 | 4×4 | 0.64 | 100 | 100 | |
| ＞3300 | ＞220 | 400 | 2.5×2.5 | 0.46 | 100 | 100 | |
| 12k twill | ＞3300 | ＞220 | 480 | 3×3 | 0.52 | 100 | 100 |
| ＞3300 | ＞220 | 560 | 3.5×3.5 | 0.56 | 100 | 100 | |
| ＞3300 | ＞220 | 680 | 4×4 | 0.64 | 100 | 100 |