NJMKT carbon fiber sheet is a kind of unidirectional carbon fiber reinforced material made by imported Toray carbon fiber filament.
Thickness: 0.111mm (200g) and 0.167mm (300g)
Width: 100mm, 150mm, 200mm, 300mm, 500mm and other special width requirements.
Application: widely used for tensile and seismic reinforcement of structural components. And it can be regarded as carbon fiber composite material when used with NJMKT-carbon fiber impregnation adhesive, which is suitable for reinforcement of concrete and wood structure, and has reached the requirements of "Reinforced Concrete Structure Design Code GB50367-2013", This product can effectively improve bearing capacity of components, seismic performance and durability.
Key Features
1.Light weight, easy for construction, low density, 23% of steel material, no increase of self-weight or section size to components
2. This flexible sheet can easily be cut according to your desired shape and have close adhesion with reinforced concrete surface, suitable for extensive shape structures
3. Small thickness, easy to overlap, excellent performance of winding and wrapping for various types of reinforcement, such as curved surface, strange-shape components, etc.
4. High tensile strength and flexibility, it can achieve the same effect of reinforced steel plate
5. Anti-acid and alkali, corrosion resistance, suitable for any harsh environment
6. The matching epoxy resin adhesive (suggested our factory manufactured carbon fiber impregnating adhesive) has good permeability, easy installation and short construction period
7. Non-toxic, non-irritating odor, environmentally safe, operation can be done in living situation
8. High tensile strength of 4-8 times of ordinary steel
NJMKT Carbon Fiber Sheet PK inferior sheet
1. Imported carbon fiber filament, excellent smoothness, easily to be cut according to your desired shape regularly
2. High tensile strength of 4-8 times of ordinary steel
3. Anti-acid and alkali, corrosion resistance, suitable for any harsh environment
4. Excellent performance of winding and wrapping for various types of reinforcement, such as curved surface, strange-shape components, etc.
5. Light weight, low density, 23% of steel material, no increase of self-weight or section size to components
It is your outstanding option to deal with the following engineering problems:
1. Increasing building service load
2. Changing usage function of engineering projects
3. Material aging
4. Concrete strength grade is lower than the design value
5. Structural cracks treatment
6. Repair and protection for in-service components in harsh environment
7. Improve seismic performance of buildings in multiple seismic area
8. Rreinforcement and repair of concrete structures because of disasters suffering and durability
9. Deficiency of concrete rebars
10. Building reinforcement and retrofit project
11.Building crack leakage
12.Chimney and coal mine reinforcement
13.Other applications: satellites, aircraft, sports, industrial products and many other reinforcement fields
unidirectional carbon fiber fabric, carbon fiber fabric, carbon fiber strengthening, carbon fiber reinforcement
unidirectional carbon fiber fabric, carbon fiber fabric, carbon fiber strengthening, carbon fiber reinforcement
Factory capability
NJMKT has our own product quality testing center and a full range of imported internationally-advanced testing equipment which is comparable with national testing center. We promise to test all materials before manufacture, only when the testing data meets the requirement, we put into production operation.
1.On-site production of carbon fiber sheet
2.Strict automatic unloading system per 100m to be off production line
3.Refuse short, narrow, insufficient materials
4.Standard specification, easily cut
Storage:
100m/roll
Carbon fiber sheet should be stored in dry and well-ventilated place and protect from sunlight.
Standard: GB50367-2013, GB50728-2011
NJMKT promises to meet the technical requirements of the following GB50367-2013 "Design code for concrete structure reinforcement" and GB50728-2011 "Technical code for safety identification of reinforcement materials for engineering structures".
| Test item | High - strength Grade Ⅰ | High - strength Grade Ⅱ | High - strength Grade Ⅲ | |
| Standard value of tensile strength (MPa) | ≥ 3400 | ≥ 3000 | ≥ 1800 | |
| Tensile modulus of elasticity (MPa) | ≥ 2.3×105 | ≥ 2.0×105 | ≥ 1.8 × 105 | |
| Elongation at break (%) | ≥ 1.6 | ≥ 1.5 | ≥ 1.3 | |
| Bending strength (MPa) | ≥ 700 | ≥ 600 | ≥ 500 | |
| Interlaminar shear strength (MPa) | ≥ 45 | ≥ 35 | ≥ 30 | |
| Positive bonding strength of fiber composite material and base material (MPa) | ≥ 2.5, cohesive failure of concrete | |||
| Brand of NJMKT sheet | MKT | XK | AN | |
| Carbon filament type | T-700-12K | T-36-12K | T-35-12K | |